UBESTA 3020GX6

Engineering Plastics
Dry as molded
  Unit Test method Measured value
Melting temperature °C  ISO 11357-3 178
Density g/cm3  ISO 1183-3 1.16
Tensile stress at yield MPa  ISO 527-1,2 125
Tensile strain at yield %  ISO 527-1,2 -
Tensile strain at break %  ISO 527-1,2 6
Flexural strength MPa  ISO 178 180
Flexural modulus MPa  ISO 178 8,100
Shore hardness D-scale -  ISO 868 -
Rockwell hardness R-scale -  ISO 2039-2 110
Impact strength (Charpy, Notched) 23 °C kJ/m2  ISO 179/1eA 21C
-40 °C kJ/m2  ISO 179/1eA 12C
Temp. of deflection under load 0.45 MPa °C  ISO 75-2 177
1.8 MPa °C  ISO 75-2 165
Moulding shrinkage (In flow direction/ In transverse direction) %  ISO 294-4 0.1/0.6
Abrasion loss (CS-17. 1,000 rev.) mg  ISO 9352 12
Coef. Of linear thermal expansion 10-4 /K  ISO 11359-2 0.2
Volume resistivity Ω·cm  IEC 60093 106
Moisture absorption (24 h in water at 23 °C) %  ISO 62 0.4
Melt flow rate(235 °C/2,160 g) g/10 min  ISO 1133 4
Comments     Injection
GF/CF
Color     Black

Impact Strength:N=not broken P=partially broken C=completely broken