Injection 3024GU6L1

Engineering Plastics
Dry as molded
Characteristic Unit Test method Measured value
Mechanical Characteristics
Tensile strength MPa  ISO 527-1,2 115
Tensile strain at break % 6.0
Tensile modulus GPa 6.7
Flexural strength MPa  ISO 178 175
Flexural modulus GPa 5.8
Charpy notched impact strength kJ/m2  ISO 179-1/1eA 24
Rockwell hardness R.Scale -  ISO 2039-2 110
M.Scale -
Thermal Characteristics
Melting temperature °C  ISO 11357 175~181
Coeff. of linear thermal expansion x10-5/°C  ISO 11359-2 3.0
Temperature of deflection under load 0.45 MPa °C  ISO 75-1,2 177
1.8 MPa °C 161
Electical Characterisitics
Volume resistivity Ωcm  JIS K6911 1015
Electric strength kV/mm  IEC 60243-1 -
Relative permittivity -  IEC 60250 -
Arc resitance s  D-495(ASTM) -
C.T.I UL index  UL746A -
Others
Density g/cm3  ISO 1183-3 1.24
Water absorption 23 °C, 50 %RH %  UBE method -
Molding shrinkage MD %  UBE method(30x100x3t) -
TD -
Nomenclature accdording to ISO 1874-1 PA12, MHR,
18-060, GF30