Engineering Plastics
Dry as molded
Characteristic Unit Test method Measured value
Mechanical Characteristics
Tensile strength MPa  ISO 527-1,2 185
Tensile strain at break % 2.5
Tensile modulus GPa 10.5
Flexural strength MPa  ISO 178 270
Flexural modulus GPa 9.8
Charpy notched impact strength kJ/m2  ISO 179-1/1eA 11
Rockwell hardness R.Scale -  ISO 2039-2 -
M.Scale -
Thermal Characteristics
Melting temperature °C  ISO 11357 215~225
Coeff. of linear thermal expansion x10-5/°C  ISO 11359-2 2.5
Temperature of deflection under load 0.45 MPa °C  ISO 75-1,2 220
1.8 MPa °C 205
Electical Characterisitics
Volume resistivity Ωcm  JIS K6911 -
Electric strength kV/mm  IEC 60243-1 -
Relative permittivity -  IEC 60250 -
Arc resitance s  D-495(ASTM) -
Others
Density g/cm3  ISO 1183-3 1.39
Water absorption 23 °C, 50 %RH %  UBE method 1.8
Molding shrinkage MD %  UBE method(30x100x3t) 0.2
TD 0.7
Nomenclature accdording to ISO 16396-1 PA6, GF33. M1HL, S14-100