MENU

UBESTA 3030JI46L

Engineering Plastics
Dry as molded
  Unit Test method Measured value
Melting temperature °C  ISO 11357-3 168
Density g/cm3  ISO 1183-3 1.00
Tensile stress at yield MPa  ISO 527-1,2 > 20
Tensile strain at yield %  ISO 527-1,2 -
Tensile strain at break %  ISO 527-1,2 > 150
Flexural strength MPa  ISO 178 10
Flexural modulus MPa  ISO 178 200
Shore hardness D-scale -  ISO 868 58
Rockwell hardness R-scale -  ISO 2039-2 21
Impact strength (Charpy, Notched) 23 °C kJ/m2  ISO 179/1eA 97P
-40 °C kJ/m2  ISO 179/1eA 5C
Temp. of deflection under load 0.45 MPa °C  ISO 75-2 71
1.8 MPa °C  ISO 75-2 43
Moulding shrinkage (In flow direction/ In transverse direction) %  ISO 294-4 1.0/1.5
Abrasion loss (CS-17. 1,000 rev.) mg  ISO 9352 30
Coef. Of linear thermal expansion 10-4 /K  ISO 11359-2 1.9
Volume resistivity Ω·cm  IEC 60093 1010
Moisture absorption (24 h in water at 23 °C) %  ISO 62 0.7
Melt flow rate(235 °C/2,160 g) g/10 min  ISO 1133 12
Comments     Tubing
Impact modified
Low migration
Color     Black

Impact Strength:N=not broken P=partially broken C=completely broken